In this work the effect of microwave irradiation on morphology and performance of polyethersulfone (PES) membranes was investigated. The membranes were prepared with 20 wt.% of PES by phase inversion method. N,N-dimethylformamide (DMF) and mixture of water and ethyl alcohol (90/10 vol.%) were employed as solvent and coagulant respectively. Polyvinylpirrolidone (PVP) with the concentration of 2 wt.% was selected as pore former. The effects of irradiation time (10, 30, 60, 90, 120 s) and microwave power (180, 360, 720 and 900 W) on structure and performance of membranes were studied. Increasing the irradiation time and power caused variation in permeate flux and ion rejection. Moreover, the effects of annealing processes (60, 70, 80 degrees C) were studied. Transmembrane pressure was selected around 1.5 MPa for all experiments. Scanning electron microscope (SEM) and atomic force microscope (AFM) were employed to describe the surface morphology of the prepared membranes. The effect of microwave irradiation time in different power revealed alterations in membrane surface morphology and AFM images represented that surface parameters (such as surface roughness) have been changed. The membrane exhibited moderate rejection (47%) and low permeate flux (4.5 kg/m(2) h) at 80 degrees C for NaCl solution. The SEM images indicate that the dense skin layer is formed at 80 degrees C annealing. (C) 2009 Elsevier B.V. All rights reserved.