Poly(lactide)-block-poly(ethylene oxide)-block-poly(lactide) (PLA-PEO-PLA) triblock copolymers are known to form physical hydrogels in water as a result of the polymer's amphiphilicity. Their mechanical properties, biocompatibility, and biodegradability have made them attractive for use as soft tissue scaffolds. However, the network junction points are not covalently cross-linked, and in a highly aqueous environment these hydrogels adsorb more water, transform from gel to sol, and lose the designed mechanical properties. In this article, a hydrogel was formed by the use of a novel two-step approach. In the first step, the end-functionalized PLA-PEO-PLA triblock was self-assembled into a physical hydrogel through hydrophobic micelle network junctions, and in the second step, this self-assembled physical network structure was locked into place by photo-cross-linking the terminal acrylate groups. In contrast with physical hydrogels, the photo-cross-linked gels remained intact in phosphate-buffered solution at body temperature. The swelling, degradation, and mechanical properties were characterized, and they demonstrated an extended degradation time (similar to 65 days), an exponential decrease in modulus with degradation time, and a tunable shear modulus (1.6-133 kPa). We also discuss the various constitutive relationships (Hookean, neo-Hookean, and Mooney-Rivlin) that can be used to describe the stress-strain behavior of these hydrogels. The chosen model and assumptions used for data fitting influenced the obtained modulus values by as much as a factor of 3.5, which demonstrates the importance of clearly stating one's data fitting parameters so that accurate comparisons can be made within the literature.