Fumed silica was used as a dopant in the preparation of poly(methyl methacrylate-acrylonitrile-vinyl acetate) (P(MMA-AN-VAc)) to improve the ionic conductivity of the P(MMA-AN-VAc)-based gel polymer electrolyte (GPE). The performance of the P(MMA-AN-VAc) membrane and its GPE for lithium ion battery use were studied by XRD, SEM, TGA, LSV. CA, EIS. and charge/discharge test. It is found that the doping of fumed silica in the P(MMA-AN-VAc) changes the membrane from semi-crystal to amorphous state and the pore structure of the membrane. By the doping of 10 wt.% fumed silica in the membrane, the porosity of the membrane increases with the pore dispersed more uniformly and interconnected and having higher electrolyte uptake, resulting in the improvement in ionic conductivity of the GPE from 3.48 x 10(-3) to 5.13 x 10(-3) S cm(-1) at ambient temperature. On the other hand, the thermal stability of the membrane, the electrochemical stability of the GPE, and the cyclic performance of the battery are also improved. (c) 2009 Elsevier Ltd. All rights reserved.