The graphite nanosheets/polyaniline (GN/PANI) nanorods composites were fabricated via ultrasonic polymerization of aniline monomer in the presence of GN, which was used as electric filling. The kind of doped acids, the concentration, and the contents of the GN were used as impact factors to the conductivity of the materials that were investigated. The structure of nanocomposites were characterized by FTIR and SEM. The results Show that ultrasonic can effectively restrain the agglomerate of the aniline and come to uniformity nanorods composites. The conductivity reached to 4.8 S/cm and 22 S/cm, respectively. The thermal stability of GN/PANI nanorods composites is superior to pure PANI as shown by TG analysis. (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 112: 573-578, 2009