The denture bases nanocomposites were prepared by adding organic montormollontrite(OMMT) into poly(methyl methacrylate) matrix. The resulting composites were characterized by XRD, TEM, and ISTRON 3365 flexural strength testing systems. One-way analysis of variance and Tukey's test were used to compare the difference in flexural strength and flexural modulus. The results showed the formation of exfoliated-intercalated and intercalated denture base nanocmposite when the content of OMMT was 3 wt % and 5 wt % in the powder of denture base resin, respectively. The maximum ultimate flexural strength was observed in denture base nanocomposite containing 3 wt % of OMMT and flexural strength decreased with further increases of OMMT content. The flexural modulus of denture base nanocomposite increased continually with OMMT content increasing from 1 wt % to 10 wt %. Significant difference in both flexural strength and flexural modulus was observed between the nanocomposites with 3 wt % OMMT and controls (n = 5, P < 0.05). (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 112: 3548-3553, 2009