Nanosized hydroxyapatite (HAP) particles were prepared by sol-gel method from the water-based solution of calcium and phosphorus precursor. In this study, two calcium precursors such as calcium nitrate tetrahydrate and calcium acetate were chosen as calcium precursors. The influence of aging period, pH, viscosity and sintering temperature on crystallinity and morphology of the HAP particles were investigated for the two calcium precursors with triethyl phosphate precursor. The morphology of nano-HAP towards phosphorous precursor was dependent on the type of calcium precursor used. The HAP prepared from calcium nitrate and triethyl phosphate was spherically shaped whereas the one from calcium acetate was found to be fibrous in structure. Both HAPs were stable up to 1200 degrees C and their crystallinity increased with respect to the sintering temperature. The obtained sample was characterized through X-ray diffraction (XRD), P-31 nuclear magnetic resonance (NMR), scanning electronic microscopy (SEM) and TEM analysis. The sol derived from the optimized aging period for the two different calcium precursors was coated on 316L stainless-steel (SS) implant and its corrosion resistivity during long-term implantation was studied by cyclic polarization in Ringer's solution. Both HAPs have their own desirable qualities and were found to be corrosion resistive. (c) 2008 Elsevier B.V. All rights reserved.