This paper has clarified the anelasticity of 8Y-FSZ/alpha-alumina composites wherein the 8Y-FSZ phases are dispersed like islands. The amount of anelastic strain generated and the manner of anelastic deformation were compared to those of monolithic 8Y-FSZ. The anelastic strains of six kinds of 8Y-FSZ/alpha-alumina, as well as of monolithic 8Y-FSZ and monolithic alpha-alumina, were measured. The results showed that the anelastic strain was produced even in the composite where 8Y-FSZ phases existed as islands, and that the more the anelastic strain produced, the higher the volume fraction of 8Y-FSZ. In addition, the composition with a fully densified alumina phase had the effect of inhibiting anelastic strain in the 8Y-FSZ phase.