The silicon phases in the spray-formed and extruded hypereutectic Al-Si alloys (AlSi18, AlSi25 and AlSi35) have been quantitatively evaluated by means of image analysis technique. The influence of silicon content in the alloys, thermal conditions during spray forming of the alloys and hot extrusion of the spray-formed alloys on the size, shape, dispersion and orientation of the silicon phases have been studied and discussed. In general, the silicon phases are greatly refined and uniformly distributed in the spray-formed Al-Si alloys. This improvement in the silicon phases is further facilitated by low thermal input as well as fast cooling conditions during spray forming. The silicon particles in the as-extruded Al-Si alloys appear more homogeneous and regular than those in the as-deposited Al-Si alloys but exhibit a certain amount of anisotropy and a tendency to preferred orientation. The silicon particles, depending on the particle size and shape, may fracture or coarsen during extrusion.