Surface tension of linear-linear and star/linear polystyrene blends were measured using a modified Wilhelmy method. Our results show that for both polystyrene blend systems, the surface tension-composition profile is convex, indicating a strong surface excess of the component with lower surface energy. Star/linear blends display more convex surface tension profiles than their linear-linear counterparts, indicative of stronger surface segregation of the branched-component relative to linear chains. As a first step toward understanding the physical origin of enhanced-surface segregation of star polymers, self-consistent field (SCF) lattice simulations (both incompressible and compressible models) and Cahn-Hilliard theory were used to predict surface tension-composition profiles. Results from the lattice simulations indicate that the highly convex surface tension profiles observed in the star/linear blend systems are only possible if an architecture-dependent, Flory interaction parameter (chi = 0.004) is assumed. This conclusion is inconsistent with results from bulk differential scanning calorimetry (DSC) measurements, which indicate sharp glass transitions in both the star/linear and linear/linear homopolymer blends and a simple linear relationship between the bulk glass transition temperature and blend composition. To implement the Cahn-Hilliard theory, pressure-volume-temperature (PVT) data for each of the pure components in the blends were first measured and the data used as input for the theory. Consistent with the experimental data, Cahn-Hilliard theory predicts a larger surface excess of star molecules in linear hosts over a wide composition range. :significantly, this result is obtained assuming a nearly neutral interaction parameter between the linear and star components, indicating that the surface enrichment of the stars is not a consequence of complex phase behavior in the bulk. (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1666-1685, 2009