Coated aluminum bipolar plates demonstrate better mechanical strength, ease of manufacturability, and lower interfacial contact resistance (ICR) than graphite composite plates in polymer electrolyte membrane (PEM) fuel cell applications. In this study, coated aluminum and graphite composite bipolar plates were installed in separate single PEM fuel cells and tested under normal operating conditions and cyclic loading. After 1000 h of operation, samples of both the bipolar plates and the membrane electrode assembly (MEA) were collected from both the cathode and the anode sides of the cell and characterized to examine the stability and integrity of the plate coating and evaluate possible changes of the ionic conductivity of the membrane due any electrochemical reaction with the coating material. Scanning electron microscope (SEM) and energy dispersive X-ray (EDX) analysis were performed on the land and valley surfaces of the reactant flow fields at both the anode and the cathode sides of the bipolar plates. The measurements were superimposed on the reference to identify possible zones of anomalies for the purpose of conducting focused studies in these locations. The X-ray diffraction (XRD) analysis of samples scraped from the anode and cathode electrodes of the MEA showed the tendency for catalyst growth that could result in power degradation. Samples of the by-product water produced during the single fuel cell operation were also collected and tested for the existence of chromium, nickel, carbon, iron, sulfur and aluminum using mass spectroscopy techniques. The EDX measurements indicated the possibility of dissociation and dissolution of nickel chrome that was used as the binder for the carbide-based corrosion-resistant coating with the aluminum substrate. (c) 2008 Elsevier B.V. All rights reserved.