A series of novel side-chain-type sulfonated poly(arylene ether ketone)s with pendant carboxylic acid groups copolymers (C-SPAEKs) were synthesized by direct copolymerization of sodium 5,5'-carbonyl-bis(2-fluorobenzenesulfonate), 4,4'-difluorobenzophenone and 4,4'-bis(4-hydroxyphenyl) valeric acid (DPA). The expected structure of the sulfonated copolymers was confirmed by FT-IR and H-1 NMR. Membranes with good thermal and mechanical stability could be obtained by solvent cast process. It should be noted that the proton conductivity of these copolymers with high sulfonation degree (DS > 0.6) was higher than 0.03 S cm(-1) and increased with increasing temperature. At 80 degrees C, the conductivity of C-SPAEK-3 (DS = 0.6) and C-SPAEK-4 (DS = 0.8) reached up to 0.12 and 0.16 S cm-1, respectively, which were higher than that of Nafion 117 (0.10 S cm(-1)). Moreover, their methanol permeability was much lower than I hat of Nafion 117. These results showed that the synthesized materials might have potential applications is (lie proton exchange membranes for DMFCs. (C) 2009 Elsevier B.V. All rights reserved.