The electrochemical activity towards hydrogen oxidation reaction (HOR) of a high performance carbon-supported Pt-Ru electrocatalyst (HP 20 wt.% 1:1 Pt-Ru alloy on Vulcan XC-72 carbon black) has been studied using the thin-film rotating disk electrode (RDE) technique. The physical properties of the Pt-Ru nanoparticles in the electrocatalyst were previously determined by transmission electron microscopy (TEM), high resolution TEM, fast Fourier transform (FFT), electron diffraction and X-ray diffraction (XRD). The corresponding compositional and size-shape analyses indicated that nanoparticles generally presented a 3D cubo-octahedral morphology with about 26 at.% Ru in the lattice positions of the face-centred cubic structure of Pt. The kinetics for HOR was studied in a hydrogen-saturated 0.5 M H2SO4 solution using thin-film electrodes prepared by depositing an ink of the electrocatalyst with different Nafion contents in a one-step process on a glassy carbon electrode. A maximum electrochemically active surface area (ECSA) of 119 m(2) g Pt-1 was found for an optimum Nafion composition of the film of about 35 wt.%. The kinetic current density in the absence of mass transfer effects was 21 mA cm(-2). A Tafel slope of 26 mV dec(-1). independent of the rotation rate and Nafion content, was always obtained, evidencing that HOR behaves reversibly. The exchange current density referred to the ECSA of the Pt-Ru nanoparticles was 0.17 mA cm(-2), a similar value to that previously found for analogous inks containing pure Pt nanoparticles. (C) 2009 Elsevier B.V. All rights reserved.