Korean Journal of Chemical Engineering, Vol.27, No.4, 1310-1315, July, 2010
Characterization and synthesis of Ce-incorporated mesoporous molecular sieves under microwave irradiation condition
E-mail:
Ce-incorporated MCM-41 mesoporous molecular sieves (CeMCM-41) were synthesized by microwave irradiation method from sodium silicate and ammonium cerium (IV) nitrate precursors and using cetyltrimethyl ammonium bromide (CTAB) as template. The resulting samples were characterized by means of XRD, TEM, FT-IR, UV-Vis, XPS and N2 physical adsorption, respectively. The effect of the Si/Ce molar ratio on the textural properties of CeMCM-41 was investigated. The results reveal that the CeMCM-41 was successfully synthesized. The resultant mesoporous materials have specific surface areas in the range of 602-1,216 m2/g and pore sizes in the range of ca. 2.6-2.9 nm. The structural properties are related to the amount of cerium incorporation. The surface area and pore volume of the resulting CeMCM-41 were gradually reduced as the cerium content in the sample increased, and the mesoporous ordering diminished.
Keywords:Ce-incorporated Mesoporous Molecular Sieve;Microwave Irradiation Method;Synthesis;Characterization;Textural Property
- Beck JS, Vartuli JC, Roth WJ, Leonowicz ME, Kresge CT, Schmitt KD, Chu CTW, Olson DH, Sheppard EW, McCullen SB, Higgins JB, Schlenker JL, J. Am. Chem. Soc., 114, 10834 (1992)
- Aoyama N, Yoshihara T, Furukawa S, Nitta T, Takahashi H, Nakano M, Fluid Phase Equilib., 257(2), 212 (2007)
- Velu S, Wang L, Okazaki M, Suzuki K, Tomura S, Microporous Mesoporous Mater., 54, 113 (2002)
- Jiang TS, Lu LD, Yang XJ, Zhao Q, J. Porous Mater., 15, 67 (2008)
- Wojcieszak R, Monteverdi S, Mercy M, Nowak I, Ziolek M, Bettahar MM, Appl. Catal. A: Gen., 268(1-2), 241 (2004)
- Kerby MC, Degnan TF, Marler DO, Beck JS, Catal. Today, 104(1), 55 (2005)
- Mary GE, Kennet JB, Microporous Mesoporous Mater., 28, 113 (1999)
- Tang Q, Xu Y, Wu D, Sun Y, Wang J, Xu J, Deng F, J. Controlled Release., 114, 41 (2006)
- Chaliha S, Bhattacharyya KG, J. Hazard. Mater., 150, 728 (2008)
- Li SM, Xu Q, Chen JF, Guo YQ, Ind. Eng. Chem. Res., 47(21), 8211 (2008)
- Chen LF, Zhou XL, Norena LE, Wang JA, Navarrete J, Salas P, Montoya A, Del Angel P, Llanos ME, Appl. Surf. Sci., 253(5), 2443 (2006)
- Jiang TS, Zhao Q, Chen KM, Tang YJ, Yu LB, Yin HB, Appl. Surf. Sci., 254(9), 2575 (2008)
- Xu JQ, Chu W, Luo SZ, J. Mol. Catal. A-Chem., 256(1-2), 48 (2006)
- Timofeeva MN, Jhung SH, Hwang YK, Kim DK, Panchenko VN, MeIgunov MS, Chesalov YA, Chang JS, Appl. Catal. A: Gen., 317(1), 1 (2007)
- Khalil KMS, J. Colloid Interface Sci., 307(1), 172 (2007)
- Lu C, Worrell WL, Gorte RJ, Vohs JM, J. Electrochem. Soc., 150(3), A354 (2003)
- Kadgaonkar MD, Laha SC, Pandey RK, Kumar P, Mirajkar SP, Kumar R, Catal. Today, 97(4), 225 (2004)
- Araujo AS, Aquino JMFB, Souza MJB, Silva AOS, J. Solid State Chem., 171, 371 (2003)
- Tanev PT, Chibwe M, Pinnavaia TJ, Nature, 368(6469), 321 (1994)
- Dai Q, Wang X, Chen G, Zheng Y, Lu G, Microporous Mesoporous Mater., 100, 268 (2007)
- Chen LF, Norena LE, Navarrete J, Wang JA, Mater. Chem. Phys., 97(2-3), 236 (2006)
- Laha SC, Mukherjee P, Sainkar SR, Kumar R, J. Catal., 207(2), 213 (2002)
- Yao WH, Chen YJ, Min L, Fang H, Yan ZY, Wang HL, Wang JQ, J. Mol. Catal. A-Chem., 246(1-2), 162 (2006)
- Chen QF, Jiang D, Shi WM, Wu D, Xu Y, Appl. Surf. Sci., 255(18), 7918 (2009)
- Reddy BM, Khan A, Yamada Y, Kobayashi T, Loridant S, Volta JC, J. Phys. Chem., 106, 10964 (2002)
- Bensalem A, Bozonverduraz F, Delamar M, Bugli G, Appl. Catal. A: Gen., 121(1), 81 (1995)