Biphenol-based, partially disulfortated poly(arylene ether sulfone)s synthesized by direct copolymerization show promise as potential reverse osmosis membranes. They have excellent chlorine resistance over a wide range of pHs and good anti-protein and anti-oily water fouling behavior. Crosslinking of these copolymers that have high degrees of disulfonation may improve salt rejection of the membranes for reverse osmosis performance. A series of controlled molecular weight, phenoxide-endcapped, 50% disuffortated poly(arylene ether sulfone)s were synthesized. The copolymers were reacted with a multifunctional epoxy resin and crosslinked thermally. The effects on network properties of various factors such as crosslinking time, copolymer molecular weight and epoxy concentration were investigated. The crosslinked membranes were characterized in terms of gel fraction, water uptake, swelling and self-diffusion coefficients of water. The salt rejection of the cured membranes was significantly higher than that for the uncrosslinked copolymer precursors. (C) 2008 Elsevier Ltd. All rights reserved.