The structure development in the continuous laser-heated drawing process of poly(ethylene 2,6-naphthalene dicarboxylate) (PEN) fiber was analyzed by in-situ X-ray diffraction measurement. Because of the rapid and uniform laser heating, and the resultant steady-state nature of the necking-drawing, the structure development after the on-set of necking could be measured in the time resolution of several hundred microseconds. We found for the first time the temporal appearance of meridional (001') diffraction at several milliseconds after the on-set of necking indicating that the mesophase structure similar to the one reported for poly(ethylene terephthalate) was also formed in the initial stage of fiber structure development of PEN. The d-spacing of the (001') diffraction 1.230 +/- 0.003 nm was shorter than the c-axis lengths of both alpha and beta crystals. (C) 2009 Elsevier Ltd. All rights reserved.