Atomised and milled Ferrosilicon with average particle diameters of 38 and 50 pm respectively were fluidised with air at ambient conditions. The entrainment rate of the more spherical atomised particles was on average six times that of the irregularly shaped milled particles over the range of superficial velocities investigated. In an attempt to decouple the effect of particle size from shape, the bed was divided into theoretically isolated bins based on the distributions of particle sizes. This indicated that the atomised particles had a higher entrainment rate for particles smaller than approximately 25 pm whereas the opposite was true for particles greater than this size. None of the entrainment correlations investigated was able to predict the switch in entrainment behaviour as a function of particle sphericity and diameter. Furthermore. the traditional critical particle diameter associated with cohesive Geldart A particles was not observed for either of the two particle shapes. It is therefore concluded that neither the hydrodynamic nor Van der Waals forces acting on the particles can adequately explain the entrainment rate behaviour of differently shaped high-density Geldart A particles. (C) 2008 Elsevier B.V. All rights reserved.