The ignition behaviour of boron powder, prepared through electrowinning process, was studied by using thermogravimetry coupled with simultaneous differential thermal analysis (TG-SDTA). The dependence of the inception of the ignition reaction on the partial pressure of oxygen, particle size of the boron powder and heating rate was investigated. It was observed that all these factors affect the ignition temperature. Boron powder with a mean particle size of about 10 mu m was found to be susceptible to ignition in oxygen even at 783K. In general, the susceptibility to ignition was found to vary inversely with the degree of crystallinity. Presence of carbon was found to retard the oxidation of boron and raise the ignition temperature. These results are useful in safe handling and storage of finely divided boron powder and in the subsequent production of boron carbide from it. (C) 2009 Elsevier B.V. All rights reserved.