In this paper, a dielectric barrier discharge operating in nitrogen at atmospheric pressure has been used to improve the surface hydrophilic property of polypropylene (PP) non-woven fabric. The changes in the hydrophilic property of the modified PP samples are investigated by the contact angle measurements and the variation of water contact angle is obtained as a function of the energy density; micrographs of the PP before and after plasma treatment are observed by scanning electron microscopy (SEM) and the chemical composition of the PP surface before and after plasma treatment is also analyzed by Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The results show that the surface hydrophilic property of the PP samples is greatly improved with plasma treatment for a few seconds, as evidenced by the fact that the contact angle of the treated PP samples significantly decreases after plasma treatment. The analysis of SEM shows that the surface roughness of the treated PP samples increases due to bonding and etching in plasma processing. The analyses of FTIR and the C1s peak in the high-resolution XPS indicate that oxygen-containing and nitrogen-containing polar functional groups are introduced into PP surface in plasma processing. It can be concluded that the surface hydrophilic property of the modified PP samples has been obviously improved due to the introduction of oxygen-containing and nitrogen-containing polar groups and the increase of the surface roughness on the PP surface. (C) 2010 Elsevier B. V. All rights reserved.