Korean Chemical Engineering Research, Vol.48, No.6, 679-683, December, 2010
Export Citation
페놀의 수산화 반응에 사용한 TS-1 촉매의 효과적인 재생 방법(소성 온도 의존성)
Regeneration of TS-1 Catalyst During Phenol Hydroxylation (Calcination temperature dependence)
권송이1, 2, 윤성훈1, 엄경섭3, 이재욱2, 이철위1, †
  • 1한국화학연구원 그린화학연구단, 305-600 대전광역시 유성구 장동 100
  • 2서강대학교 화공생명공학과, 121-742 서울시 마포구 신수동 1
  • 3선경워텍(주), 689-896 울산광역시 울주군 온산읍 화산리 322
Song Yi Kwon1, 2, Songhun Yoon1, Kyung Sub Um3, Jae Wook Lee2, and Chul Wee Lee1, †
  • 1Green Chemistry Division, KRICT, P.O. Box 107, Yusung-gu, Daejeon 305-600, Korea
  • 2Department of Chemical and Biomolecular Engineering, Sogang University, 1 Sinsu-dong, Mapo-gu, Seoul 121-742, Korea
  • 3Sunkyung Watech, 322, Hwasan-ri, Onsan-eup, Ulju-gun, Ulsan 689-896, Korea
E-mail:
초록
본 연구에서는 과산화수소수에 의한 페놀의 수산화 반응에서 사용한 TS-1 촉매를 효과적으로 재사용할 때, 소성 온도가 촉매의 특성에 미치는 영향에 대해서 연구하였다. TS-1 촉매를 5회 재생시켜 반복 사용하였는데, 매회 마다 550 ℃ 및 700 ℃에서 각각 소성하였다. Fresh한 촉매의 페놀 전환율은 22.9%이었는데, 550 ℃에서 소성한 촉매에서는 5회 재생하였을 때 15.1%로 감소하였고, 700 ℃에서 소성한 촉매는 5회 재생하였을 때 18.8%로 감소하였다. 그리고 카테콜/하이드로퀴논의 생성비가 550 ℃에서 5회 재생 후에는 1.45, 700 ℃에서 5회 재생 후에는 1.2가 되었다. 소성 온도에 따른 재생 전·후 촉매에 대한 XRD, UV-vis spectra, N2 흡착/탈착 시험, TGA 등과 같은 특성 분석 및 촉매 성능(페놀전환율 및 생성물의 선택도)을 비교함으로써 촉매의 비활성화 원인을 예측하였다.
In this study, calcination temperature dependence of TS-1 catalyst was investigated in the hydroxylation of phenol with hydrogen peroxide during the regeneration of catalyst. Catalyst was regenerated 5 times by calcining at 550 ℃ and 700 ℃, respectively. When the catalyst was regenerated at 550 ℃ after 5th regeneration phenol conversion was decreased from 22.9% to 15.1% and at 700 ℃ after 5th regeneration phenol conversion was decreased from 22.9% to 18.8%. For formation ratio of catechol/hydroquinone was increased from 1.28 to 1.45 after 5th regeneration at 550 ℃, and from 1.28 to 1.20 after 5th regeneration at 700 ℃. The main reasons for deactivation of the catalyst were suggested by analyzing chemical/physical properties with XRD, UV-vis spectra, N2 adsorption/desorption and TGA, and evaluating the catalytic activity such as phenol conversion and product selectivity.
Keywords:Phenol;Hydrogen Peroxide;TS-1;Regeneration;Calcination
  1. Taramasso M, Perego G, Notari B, U.S. Patent No. 4,410,501 (1983)
  2. Clerici MG, Bellussi G, Romano U, J. Catal, 129, 159 (1991)
  3. Kannan S, Dubey A, Knozinger H, J. Catal., 231(2), 381 (2005)
  4. Liu H, Lu GZ, Guo YL, Guo Y, Wang JS, Chem. Eng. J., 108(3), 187 (2005)
  5. Zhang XJ, Wang Y, Xin F, Appl. Catal. A: Gen., 307(2), 222 (2006)
  6. Thangaraj A, Kumar R, Mirajkar SP, Ratnasamy P, J. Catal., 130, 1 (1991)
  7. Tuel A, Moussa-Khouzami S, Taarit YB, Naccache C, J. Mol. Catal., 68, 45 (1991)
  8. Wilkenhoner U, Langhendries G, van Laar F, Baron GV, Gammon DW, Jacobs PA, van Steen E, J. Catal., 203(1), 201 (2001)
  9. Wang XS, Guo XW, Li G, Catal. Today, 74(1-2), 65 (2002)
  10. Serrano DP, Sanz R, Pizarro P, Moreno I, de Frutos P, Blazquez S, Catal. Today, 143, 151 (2009)
  11. Cheneviere Y, Chieux F, Caps V, Tuel A, J. Catal., 269, 161 (2010)
  12. Vayssilov GN, Catal. Rev.-Sci. Eng., 39(3), 209 (1997)