Mesoporous carbon (MC) samples having especially high specific surface area, pore size, and pore volume (e.g. pore volume in excess of 4 cm(3) g(-1)) were prepared and their suitability as Pt catalyst supports in polymer electrolyte membrane fuel cells was examined. Pt particles on the MC support were slightly larger than those on commercial samples of Pt on carbon black, and they showed a greater tendency to agglomerate on the MC support than on carbon black. Ex situ cyclic voltammetry gave values for electrochemically active surface area that were about half that for a commercial Pt-on-carbon black sample. Preliminary attempts to prepare thin-film electrodes from Pt/MC samples with a Nafion binder using conventional ink formulations failed, probably because much of the Nafion electrolyte was taken up inside support pores and was not available to bind the support particles together. An alternate approach involving painting of catalyst inks directly onto gas diffusion layers was used to prepare membrane electrode assemblies (MEAs) from Pt/MC samples, which were tested using single-cell test hardware. Performance of these Pt/MC sample MEAs was compared with that prepared by decal transfer method with commercially obtained Vulcan XC-72R supported Pt catalyst. The reasons for the lower performance of Pt/MC were discussed. (C) 2009 Elsevier Ltd. All rights reserved.