Two types of microfibrillated cellulose (MFC) were prepared using either a sulfite pulp containing a high amount of hemicellulose (MFC 1) or a carboxymethylated dissolving pulp (MFC 2). MFC gels were then combined with amylopectin solutions to produce solvent-cast MFC-reinforced amylopectin films. Tensile testing revealed that MFC 2-reinforced films exhibited a more ductile behavior and that MFC 1-reinforced films had higher modulus of elasticity (E-modulus) at MFC loadings of 50 wt % or higher. Pure MFC films had relatively low oxygen permeability values when data were compared with those for a variety of other polymer films. MFC 1 and MFC 2 films had similar opacity but differences in appearance which were attributed to the presence of some larger fibers and nanofiber agglomerates in MFC 2. Field emission scanning electron microscopy (FE-SEM) and atomic force microscopy (AFM) were used to illustrate the morphology of MFC nanofibers in pure films and in an amylopectin matrix. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 1:17: 3601-3609, 2010