The effect of processing method and condition on the dispersion status of multiwalled carbon nanotubes (MWCNTs), and mechanical properties of the MWCNT/polyamide 6 (PA6) composites are investigated. Different melt processing conditions are used to dilute the master batch produced by melt process or in situ polymerization. Both MWCNTs and carboxyl group functionalized MWCNTs (MWCNTs-COOH) are compounded with PA6 at different loadings (0.1, 0.25, 0.5, and 0.75 wt %) to study the effect of chemical modification of MWCNTs on the mechanical properties of the final composites. It is demonstrated that chemical modification of MWCNTs has a positive effect on the strength of the composites as an increase of 5-10 MPa was observed. More importantly, a near 5 MPa increase in strength and more importantly, a maximum of 138% increase in strain at break were observed for the composites produced by in situ polymerization, indicating a toughening and strengthening effect of CNT on the composites. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 120: 133-140, 2011