Korean Journal of Chemical Engineering, Vol.28, No.4, 1133-1138, April, 2011
X-ray photoelectron spectroscopic characterization of molybdenum nitride thin films
E-mail:
The elemental composition and chemical states of a series of Mo nitride thin films have been investigated using x-ray photoelectron spectroscopy (XPS). The chemical composition and stoichiometry of the films were also tracked as a function of the preparative parameters: the nitrogen ion dose, ion accelerating energy and substrate temperature. At the lowest ion dose, the Mo concentration increased to a depth of ~300 A. The nitrogen concentration in the film decreased with increasing the ion energy. An increase in the ion energy to 100 and 200 kV led to a lower N/Mo ratio as compared to that at 50 kV. The magnitude of the binding energy separation at room temperature was smaller than that at higher temperatures. This difference might be due to the presence of B1-MoN at higher temperatures and the existence of δ-MoN at lower temperatures.
  1. Choi JG, J. Kor. Cry. Tech., 20, 74 (2010)
  2. Choi JG, J. Kor. Cry. Tech., 20, 80 (2010)
  3. Sajkowski DJ, Oyama ST, Prep. Petrol. Chem. Div., 199th ACS Nat. Meeting (1990)
  4. Oyama ST, Schlatter JC, Metcalfe JE, Lambert JM, Ind. Eng. Chem. Res., 27, 1639 (1988)
  5. Choi JG, J. Ind. Eng. Chem., 8(1), 1 (2002)
  6. Choi JG, Kim JS, J. Ind. Eng. Chem., 7(5), 332 (2001)
  7. Volpe L, Boudart M, J. Phys. Chem., 90, 4874 (1986)
  8. Choi JG, Choi D, Thompson LT, J. Mater. Res., 7, 374 (1992)
  9. Briggs D, Seah MP, Practical Surface Analysis by Auger and X-ray Photoelectron Spectroscopy., Wiley, New York (1983)
  10. Marest G, Hyperfine Interactions., 111, 121 (1998)
  11. Lin WL, Kheyrandish H, Colligon JS, Mater. Sci. Eng., B1, 165 (1988)
  12. Grabowski KS, Kahn ADF, Dovovan EP, Carosella CA, Nucl. Instr. Meth. Phys. Res., B39, 190 (1989)
  13. Bussman U, Meerbach FHJ, Te Kaat EH, Nucl. Instr. Meth.Phys. Res., B39, 230 (1989)
  14. Saito K, Asada Y, J. Phys., F17, 2273 (1987)
  15. Choi JG, Choi D, Thompson LT, Appl. Surf. Sci., 108, 103 (1997)
  16. Choi JG, Thompson LT, Appl. Surf. Sci., 93, 143 (1996)
  17. Choi JG, Brenner JR, Thompson LT, J. Catal., 154(1), 33 (1995)
  18. Piette M, Terwagne G, Moller W, Bodart F, Mater. Sci. Eng., B2, 189 (1989)