We have obtained high-quality, crack-free AlN wafers using a convex thermal field inside the growth chamber. Free-standing AlN boules of 15 mm in height and 15 mm in diameter were grown. The carbon concentration was found to be similar in all parts of the boule (similar to 8 x 10(18) cm(-3)) while the initial O concentration was higher (similar to 1 x 10(19) cm(-3)) and slightly decreased during growth. It was found that O incorporated differently on different crystallographic faces. High resolution XRD showed a continuous improvement in crystal quality as a function of boule length. The full width at half maximum (FWHM) of the double crystal rocking curves decreased from 78 in at the beginning of growth to 13 in at the growth end. To the best of our knowledge, this is the first report on impurity incorporation on different crystallographic facets obtained from the same boule. (C) 2010 Elsevier B.V. All rights reserved.