Homopolymer bearing cyclic carbonate (CC) group, ABA type triblock copolymers, and (AC)B(AC) type terpolymers with statistical arrangement of A and C monomers bearing side chain CC groups are reported here. Difunctional poly(ethylene glycol) macroinitiators (PEGMIs) were prepared from PEG of three different molecular weights. PEGMIs were subsequently used for the preparation of polymers bearing CC pendant groups from cyclic carbonate methacrylate (CCMA) under atom transfer radical polymerization to yield polymers with low polydispersity index. Homopolymer and ABA type triblock copolymers were obtained by polymerizing CCMA monomer and (AC)B(AC) type statistical terpolymers were obtained when methyl methacrylate was included as a comonomer. No polymer was obtained when styrene was used as comonomer. The cyclic carbonate groups were subjected to ring-opening reaction with monoamine to yield side chain hydroxyurethane polymers with increased solubility and diamines to yield crosslinked insoluble materials. Changes in wettability characteristics were studied by following the water contact angle of the polymers before and after ring-opening reaction involving the cyclic carbonate pendant group. The polymers which composed of electrolyte in the form of PEG and coordinating species in the form of pendant cyclic carbonate groups showed conductivity in the range of 2-5 x 10(-6) Scm(-1) at 23 degrees C after doping with lithium bis(trifluoromethane)sulfonimide as characterized by impedance spectroscopy. (C) 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 1622-1632, 2010