Hierarchically structured spongy meso-macroporous aluminosilicates with high tetrahedral aluminum content were synthesized from a mixture of single molecular alkoxide precursor, (sec-BuO)(2)-Al-O-Si(OEt)(3), already containing Si-O-Al bonds, and a silica coreactant, tetramethoxysilane (TMOS). The spontaneous byproduct templated macroporous structure formation has been directly visualized using in situ high-resolution optical microscopy (OM), allowing the crucial observation of a microbubble dispersion which is directly correlated to the macrostructure observed by electronic microscopies (SEM and TEM). This discovery leads to a comparative study with meso macroporous pure metal oxide and to a proposal of the formation mechanism of meso macroporous aluminosilicates with 3D interconnectivity. The aluminosilicate phase/microbubbles emulsion is produced by a phase separation process occurring between the aluminosilicate nanoparticles and the liquid hydrolysis condensation reaction byproducts (water, methanol, ethanol, and butanol). The use of alkoxysilane improves the heterocondensation rates between the highly reactive aluminum alkoxide part of the single precursor and added silica species but, above all, leads to the spontaneous generation of an unusual meso-macroporosity in alkaline media. The particles obtained at pH = 13.0 featured regular micrometer-sized macrospheres separated by very thin mesoporous walls and connected by submicrometric openings, providing a 3D interconnectivity. The slight increase in pH value to 13.5 induced significant modifications in morphology and textural properties due to the slower gelification process of the aluminosilicate phase, resulting in the formation of an aluminosilicate material constituted of 1-2 mu m large independent hollow mesoporous spheres.