Preparation of SiC/C Composite Sheet from Polycarbosilane/CarbonBased Resin Mixture
SiC/C composites were prepared from a mixture of polycarbosilane and phenolic resin with weight ratio of 2/1 and 1/1 using PVB as a binder. The two types of green bodies which were formed by mould pressing method were treated in the temperature range from 1,000℃ to 1,500℃ under nitrogen. X-ray diffraction patterns, density, flexural strength and fracture surfaces of the composite were examined. The flexural strength of the composites at room temperature increased with heat-treatment temperature and showed a maximum value of 175 MPa at 1,300℃. When the composite was heat treated at 1,400℃, the flexural strength decreased rapidly due to the crystallization of SiC. The SiC/C composites showed good oxidation resistance up to 830 ℃. The effective mixing ratio of PCS/phenolic resin to obtain improved mechanical property was 2/1.
- Dutta S, "Ceramic Transaction," Ed. J.D. Cawley, 2,201, Am. Cerm. Soc., Inc., Ohio, U.S.A. (1987)
- Hasegawa Y, Okamura K, J. Mater. Sci. Lett., 4, 356 (1985)
- Hasegawa Y, Okamura K, J. Mater. Sci., 15, 720 (1983)
- Hasegawa Y, Okamura K, J. Mater. Sci., 18, 3633 (1983)
- Hirai T, Goto T, Kaji T, "New Functional Fiber Application Hand Book," 141 (1988)
- Ishikawa T, Shibuya M, Yamamura T, J. Mater. Sci., 25, 2814 (1990)
- Kawamura K, J. Ceram. Soc. Jpn., 99, 1156 (1990)
- Kodama H, Miyoshi T, J. Am. Ceram. Soc., 73, 3081 (1990)
- Narita E, "New Functional Fiber Application Hand Book," 140 (1988)
- Okabe Y, Hejo J, Kato A, J. Less Commun. Mater., 68, 29 (1979)
- Verbeek W, Winter G, "Silicon Carbide-Shaped Article and Process for the Manufacture Thereof," Ger. Offen., 2,236,078 (1974)
- Yajima S, Hasegawa Y, Hayashi J, Limura M, J. Mater. Sci., 13, 2569 (1978)
- Yajima S, Shishido T, Okamura K, Am. Ceram. Soc. Bull., 56, 1060 (1977)
- Yoshida K, Ceram. Soc., 92, 392 (1984)