Al-doped ZnO (AZO) and (Al, Na) co-doped ZnO (ANZO) thin films were prepared via sol-gel technique with an annealing process at temperatures between 450 and 550 degrees C for 60 min in air ambient, and their structural and optical properties have been investigated. The deposited films exhibited hexagonal zinc oxide structure except annealing at 450 degrees C. For the 500 degrees C-annealed samples, the surface morphology was analyzed via scanning electron microscopy, Photoluminescence (PL) of different Na content ANZO thin films showed that there were very obvious violet and blue emission bands between 400 and 500 nm, and intensity of which were enhanced with Na content increasing. Transparency of the films was improved along with increasing Na content. The result of UV indicated the absorb bands appeared obviously red shift with Na doping into ZnO, the optical gaps of all films far beyond 3.37 eV of pure ZnO, and gradually decreased with Na content increasing, this is very virtual for improving photoelectricity performance of transparent conduct oxide (TCO) film. The possible origins responsible for structure and optical properties also had been discussed. (C) 2010 Elsevier B.V. All rights reserved.