Nanocrystalline Al1-xFexN films were fabricated using the reactive sputtering method. A large amount of spin-glass-like moments are in the films. With the decrease of temperature, the films turn from the spin-glass-like behavior to ferromagnetism. At low temperatures, the saturation magnetization increases and the coercivity decreases with the increase of x. The coercivity increases significantly below 50K due to the pinning effect of the frozen disordered spin-glass-like moments. All of the films are semiconducting. The low-temperature transport mechanism turns from tunneling to hopping as x increases. Magnetoresistance (MR) shows weak saturation trend with the applied field because of the hard alignment of the frozen moments. Meanwhile, MR follows the relation of log vertical bar MR vertical bar = a + bT(-1), and the spin polarization satisfies P(T) = P(0)e(-beta T alpha), related with the disordered spin-glass-like moments. (C) 2011 Elsevier B. V. All rights reserved.