SiC reinforced copper composite coatings were prepared by electro-brush plating with micron-size silicon carbide (SiC) ranging from 1 to 5 mu m on pure copper sheet in this paper. The micro-structural characterizations of SiC/Cu composite coatings were performed by optical microscope and Scanning Electron Microscope (SEM) coupled with spectrometer, to study co-deposition mechanism of SiC/Cu. It was found that there were three different patterns of SiC deposition in plating layers during electro-brush plating process, i.e. the particles could deposit inside copper grains, in grain boundaries, or in holes of the surface. To investigate deposition mechanism of each pattern, size of SiC and copper grains was compared. By comparison of size of copper grains and hard particles, SiC were either wrapped in copper grains or deposited in grain boundaries. Moreover, electro-brush plating layers at different brush velocities and current densities were obtained respectively, to analyze the microstructure evolution of the composite coatings. The hardness of plating layers was measured. The results indicated at the current density of 3 A/dm(2), the SiC/Cu coating was compact with SiC content at a high level and the hardness reached a maximum. (C) 2011 Elsevier B.V. All rights reserved.