We developed a new electrochromic device by using compact Prussian blue (PB)/antimony tin oxide (ATO) nano-composites as anodic electrode and viologen anchoring on titanium dioxide (TiO2) nano-particles as cathodic electrode. The anodic electrode was based on a transparent nanostructured ATO nano-particle film and was electro-deposited by Prussian blue to form compact Prussian blue/ATO nano-composites by means of galvanostatic electrodeposition process. Nanocrystalline TiO2 thin films on conducting glass were modified with a mono-layer of viologen with two anchoring groups, which were much strongly adsorbed onto the surface of TiO2 nano-particles. A polymer gel electrolyte sandwiched between the anodic and cathodic layers is used as the ionic transport layer. The 2.5 cm x 2.5 cm electrochromic device shows high contrast (64.8%, at 600 nm) very low transmittance at colored stage (0.1%, at 600 nm), fast switching time (600 and 720 ms for coloration and bleaching, respectively), high coloration efficiency of 912 cm(2) C-1 at 600 nm and good stability. The enhanced performance of the electrochromic device can be attributed to the ATO nano-particles as inter-conductive materials. (C) 2011 Elsevier Ltd. All rights reserved.