An electrochemical method has been developed for the probing of hydrogel-based molecularly imprinted polymers (HydroMIPs) on the surface of a glassy carbon electrode. HydroMIPs designed for bovine haemoglobin selectivity were electrochemically characterised and their rebinding properties were monitored using cyclic voltammetry. The electrochemical reduction of bovine oxyhaemoglobin (BHb) in solution was observed to occur at -0.460 V vs (Ag/AgCl) in 150 mM phosphate buffer solution (PBS). When the protein was selectively bound to the MIP, the electrochemical reduction of oxyhaemoglobin could be observed at a similar peak potential of -0.480 V vs (Ag/AgCl). When analysing the non-imprinted control polymer (NIP) interfaced at the electrode, which contained no protein, the peak reduction potential corresponded to that observed for dissolved oxygen in solution (-0.65 V vs (Ag/AgCl)). MIP and NIP (in the absence of protein) were interfaced at the electrode and protein allowed to diffuse through the polymers from the bulk solution end to the electrode. It was observed that whereas NIP exhibited a protein response within 10 min of protein exposure, up to 45 min of exposure time was required in the case of the MIP before a protein response could be obtained. Our results suggest that due to the selective nature of the MIP, BHb arrival at the electrode via diffusion is delayed by the MIP due to attractive selective interactions with exposed cavities, but not the NIP which is devoid of selective cavities. (C) 2011 Elsevier Ltd. All rights reserved.