Industrial & Engineering Chemistry Research, Vol.51, No.1, 327-334, 2012
Systematic Investigation of Dispersions of Unmodified Inorganic Nanoparticles in Organic Solvents with Focus on the Hansen Solubility Parameters
Dispersions of unmodified nanoparticles (titanium dioxide, hydroxyapatite) were prepared by redispersion of nanoparticle powders in organic solvents using an ultrasound treatment. The dispersion quality was judged by dynamic light scattering (DLS) measurements and visual evaluation. Whereas "bad" solvents led to no or unstable dispersions with large particle diameters, dispersions made from the "good" solvents consisted of particles with relatively small diameters and were stable for several days or longer. For titanium dioxide, mixtures from four of the "good" solvents identified after first screening of a large set of solvents were prepared and tested as dispersion agent. Thus obtained dispersions showed superior properties compared to the previous dispersions, with small particles sizes and good long-time stability. Based on a rating of solvent quality and by calculation using the software HSPiP v3, the Hansen solubility parameters of the particles were then determined. Subsequently, entirely new solvent mixtures that could best fit these parameters were selected and found to also exhibit suitable properties as dispersion agent for the nanoparticles. The same iterative and quantitative approach worked also for the preparation of good and stable dispersions of hydroxyapatite. All results show that this is a promising methodology to disperse inorganic nanoparticles into suited organic solvents, for instance for the preparation of new polymeric nanocomposites. Furthermore, the method can be used to indirectly characterize the surface chemistry of nanoparticles.