In this study, lithium thio-germanate thin film electrolytes have been successfully prepared by radio frequency (RF) magnetron sputtering deposition in Ar gas atmospheres. The targets for RF sputtering were prepared by milling and pressing appropriate amounts of the melt-quenched starting materials in the nLi(2)S+GeS2 (n = 1, 2, and 3) binary system. Approximately 1 mu m thin films were grown on Ni coated Si (Ni/Si) substrates and pressed CsI pellets using SOW power and 25 mtorr (similar to 3.3 Pa) Ar gas pressures to prepare samples for Raman and Infrared (IR) spectroscopy, respectively. To improve the adhesion between the silicon substrate and the thin film electrolyte, a sputtered Ni layer (similar to 120 nm) was used. The surface morphologies and thickness of the thin films were determined by field emission scanning electron microscopy (FE-SEM). The structural properties of the starting materials, target materials, and the grown thin films were examined by X-ray diffraction (XRD), Raman, and IR spectroscopy.