Transparent aqueous sols of colloidal tetramethylammonium niobate nanocrystals were synthesized by mixing tetramethylammonium hydroxide (TMAOH), niobium ethoxide, and water at TMAOH/Nb >= 0.7 at room temperature. The X-ray diffraction patterns of the thin films prepared by evaporating the colloidal solutions on a glass substrate indicated that the colloidal niobate had a layered crystalline structure. Two types of layered structures are known as a layered niobate, i.e. M(4)Nb(6)O(17)center dot nH(2)O and MNb(3)O(8) (M = H, H(3)O, or alkaline metal). Raman spectra and electron diffraction suggested that the niobate nanocrystals were similar in crystal structure to M(4)Nb(6)O(17)center dot nH(2)O compounds. Moreover, when niobium oxide thin films were fabricated from the niobate colloidal solutions by the sol-gel method, oriented T-Nb(2)O(5) thin films, whose c-axis was parallel to the substrate surface, were obtained. The orientation of the thin films was probably attributed to the layered structure of the colloidal niobate nanocrystals. (C) 2011 Elsevier Inc. All rights reserved.