TaNx thin films were grown at temperatures ranging from 200 to 375 degrees C using atomic layer deposition (ALD). Pentakis(dimethylamino)tantalum (PDMAT) was used as a tantalum source with either ammonia or monomethylhydrazine (MMH) as a nitrogen co-reactant. Self-limiting behaviour was observed for both ammonia and MMH processes, with growth rates of 0.6 and 0.4 angstrom/cycle, respectively at 300 degrees C. Films deposited using ammonia were found to have a mono-nitride stoichiometry with resistivities as low as 70 m Omega cm. In contrast, films deposited using MMH were found to be nitrogen rich Ta3N5 with high resistivities. A Quartz Crystal Microbalance (QCM) was used to measure mass gain and loss during the cyclic ALD processes and the data was used in combination with medium energy ion scattering (MEIS) to elucidate the PDMAT absorption mechanisms. (C) 2011 Elsevier B.V. All rights reserved.