In this study, betamethasone disodium phosphate-loaded microparticles were fabricated for sustained release using poly(lactide-co-glycolide) (PLGA) by spray drying and emulsion solvent evaporation/extraction techniques. Encapsulation efficiencies ranged from 59-80% using a water-in-oil-in-oil (W/O/O) double emulsion technique and more than 90% for a spray-drying method were obtained. This was a significant improvement compared to fabrication by a water-in-oil-in-water (W/O/W) double emulsion process, which had an encapsulation efficiency of less than 15%. Multiple-phase and biphasic release profiles were observed for microparticles of PLGA 50/50 and PLGA of higher lactide contents, respectively. The PLGA 50/50 hollow microparticles fabricated using the W/O/O double emulsion technique provided a sustained release of betamethasone disodium phosphate over 3 weeks.