The prolonged delivery of hydrophilic drug salts from hydrophobic polymer carriers at high drug loading is an ambitious goal. Pamidronate disodium salt (APD) containing implants prepared from spray-dried microparticles were investigated using a laboratory ram extruder. An APD-containing polymer matrix consisting of an APD-chitosan implant embedded in the biodegradable polymer D, L-poly(lactide-co-glycolide acid-glucose) (PLG-GLU) was compared with a matrix system with the micronized drug distributed in the PLG-GLU. The APD-chitosan matrix system showed a triphasic release behaviour at loading levels of 6.86 and 15.54% (w/w) over 36 days under in-vitro conditions. At higher loading (31.92%), a drug burst was observed within 6 days due to the formation of pores and channels in the polymeric matrix. In contrast, implants containing the micronized drug showed a more continuous release pro. le over 48 days up to a loading of 31.78% (w/w). At a drug loading of 46.17% (w/w), a drug burst was observed. Using micronized drug salts and reducing the surface area available for diffusion, parenteral delivery systems for highly water-soluble drug candidates were shown to be technically feasible at high drug loadings.