Chitosan microspheres cross-linked with three different cross-linking agents viz, tripolyphosphate (TPP), formaldehyde (FA) and gluteraldehyde (GA) have been prepared by spray drying technique. The influence of these cross-linking agents on the properties of spray dried chitosan microspheres was extensively investigated. The particle size and encapsulation efficiencies of thus prepared chitosan microspheres ranged mainly between 4.1-4.7 mu m and 95.12-99.17%, respectively. Surface morphology, % erosion, % water uptake and drug release properties of the spray dried chitosan microspheres was remarkably influenced by the type (chemical or ionic) and extent (1 or 2% w/w) of cross-linking agents. Spray dried chitosan microspheres cross-linked with TPP exhibited higher swelling capacity, % water uptake, % erosion and drug release rate at both the cross-linking extent (1 and 2% w/w) when compared to those cross-linked with FA and GA. The sphericity and surface smoothness of the spray dried chitosan microspheres was lost when the cross-linking extent was increased from 1 to 2% w/w. Release rate of the drug from spray dried chitosan microspheres decreased when the cross-linking extent was increased from 1 to 2% w/w. The physical state of the drug in chitosan-TPP, chitosan-FA and chitosan-GA matrices was confirmed by the X-ray diffraction (XRD) study and found that the drug remains in a crystalline state even after its encapsulation. Release of the drug from chitosan-TPP, chitosan-FA and chitosan-GA matrices followed Fick's law of diffusion.