dGe nanofilms were deposited from aqueous solutions using the electrochemical analog of atomic layer deposition (ALD). Direct electrodeposition of Ge from an aqueous solution is self-limited to a few monolayers, depending on the pH. This report describes an E-ALD process for the growth of Ge films from aqueous solutions. The E-ALD cycle involved inducing a Ge atomic layer to deposit on a Te atomic layer formed on Ge, via underpotential deposition (UPD). The Te atomic layer was then reductively stripped from the deposit, leaving the Ge and completing the cycle. The Te atomic layer was bait for Ge deposition, after which the Te was switched out, reduced to a soluble telluride, leaving the Ge (one "bait and switch" cycle). Deposit thickness was a linear function of the number of cycles. Raman spectra indicated formation of an amorphous Ge film, consistent with the absence of a XRD pattern. Films were more stable and homogeneous when formed on Cu substrates, than on Au, due to a larger hydrogen overpotential, and the corresponding lower tendency to form bubbles.