A universal strategy was developed for the preparation of high-temperature-stable carbon nanotube (CNT) -supported metal nanocatalysts by encapsulation with a mesoporous silica coating. Specifically, we first showed the design of one novel catalyst, Pt(@)CNT/SiO(2), with a controllable mesoporous silica coating in the range 11-39 nm containing pores approximate to 3 nm in diameter. The hollow porous silica shell offers a physical barrier to separate Pt nanoparticles from contact with each other, and at the same time the access of reactant species to Pt was not much affected. As a result, the catalyst showed high thermal stability against metal particle agglomeration or sintering even after being subjected to harsh treatments up to 500 degrees C. In addition, degradation in Catalytic activity was minimized for the hydrogenation of nitrobenzene over the catalyst treated at 300 degrees C for 2 h. The scheme was also extended to coat porous silica onto the surfaces of CuRu(@)CNT and the resultant catalyst thereby can be reusable at least four times without loss of activity for the hydrogenolysis of glycerol. These results suggest that the as-prepared nanostructured CNT-supported catalysts may find promising applications, especially in conditions.