The growth of stoichiometric CuInSe2 (CIS) on Au substrates using electrochemical atomic layer deposition (E-ALD) is reported here. Parameters for a ternary E-ALD cycle were investigated and included potentials, step sequence, solution compositions and timing. CIS was also grown by combining cycles for two binary compounds, InSe and Cu2Se, using a superlattice sequence. The formation, composition, and crystal structure of each are discussed. Stoichiometric CIS samples were formed using the superlattice sequence by performing 25 periods, each consisting of 3 cycles of InSe and 1 cycle of Cu2Se. The deposits were grown using 0.14, -0.7, and -0.65 V for Cu, In, and Se precursor solutions, respectively. XRD patterns displayed peaks consistent with the chalcopyrite phase of CIS, for the as-deposited samples, with the (112) reflection as the most prominent. AFM images of deposits suggested conformal deposition, when compared with corresponding image of the Au on glass substrate.