Poly(N-isopropylacrylamide) (PNIPAM) hydrogels and the corresponding linear homopolymers were synthesized in different methanol-water mixtures (x(m) = 0, 0.13, 0.21, 0.31, 0.43, 0.57, and 0.76, where x(m) is the mole fraction of methanol) in the presence of 0.1 M Y(OTf)(3) Lewis acid. The isotacticity (meso dyad (m), %) and cloud-point temperature of these homopolymers were gradually increased and decreased, respectively, with the increase in the x(m) values of the synthesis solvent mixtures. Moreover, the corresponding linear PNIPAM homopolyrners prepared in the absence of Y(OTf)(3) showed an almost constant isotacticity of m = 45% and a cloud-point temperature of 33.0 degrees C. A SEM study revealed that the resulting hydrogels were highly porous except for the gels prepared at x(m) = 0 and 0.76. The swelling ratios of these hydrogels in water at different temperatures and in different methanol-water mixtures at 20 degrees C and the deswelling rate and the reswelling rate of these hydrogels were studied. All of these swelling results were compared with that of the corresponding gels prepared in the absence of a Lewis acid (Biswas, C. S.; Patel, V. K.; Vishwakarma, N. K.; Mishra, A. K.; Bhimireddi, R.; Rai, R.; Ray, B. J. Appl. Polym. Sci. 2012, DOI: 10.1002/app.36318) and explained on the basis of the porosity of the gel, the state of aggregation and isotacticity of the PNIPAM chain segment, and the cononsolvency of the methanol-water mixture toward the PNIPAM chain segment.