Polymer Engineering and Science, Vol.52, No.2, 431-437, 2012
Preparation and property of 2-acrylamide-2-methylpropanesulfonic acid/acrylamide/sodium styrene sulfonate as fluid loss agent for oil well cement
A novel terpolymer 2-acrylamide-2-methylpropanesulfonic acid/acrylamide/sodium styrene sulfonate (AMPS/AM/SSS), used as fluid loss agent for oil well cement under high temperature, was prepared with initiator of azobisisobutryamide chloride. The optimum reaction conditions of polymerization were obtained from the orthogonal experiments, reaction temperature 40 degrees C, initiator 0.1 wt%, molar ratio of monomers AMPS/AM/SSS 20/5/1. The structure and performance of terpolymer was characterized with Fourier transform infrared spectrometer, nuclear magnetic resonance hydrogen spectrum, thermogravimetric and simultaneous differential thermal analysis, high-temperature and high-pressure water loss meter, and rotational viscometer, indicating that the terpolymer was perfectly synthesized and started to decompose at 350 degrees C and showed good performance of fluid loss control up to 160 degrees C. The -potential instrument and scanning electron microscopy were used to investigate the mechanisms of fluid loss control, indicating that the terpolymer can prevent the generation of flocculated structure in the cement and reduce the porosity of the filter cake. These results have important referential value for developing new high-temperature-resisting fluid loss agents. POLYM. ENG. SCI., 2012. (C) 2011 Society of Plastics Engineers