This article is concerned with understanding the behavior of polyethylene terephthalate (PET) in the injection stretch blow molding (ISBM) process where it is typically biaxially stretched to form bottles for the packaging industry. A comprehensive experimental study was undertaken, analyzing the behavior of three different grades of PET under constant width (CW), simultaneous (EB), and sequential (SQ) equal biaxial deformation. Experiments were carried out at temperature and strain rate ranges of 80-110 degrees C and 1 s-1 to 32 s-1, respectively, to different stretch ratios. Results show that the biaxial deformation behavior of PET exhibits a strong dependency on forming temperature, strain rate, stretch ratio, deformation mode, and molecular weight. The tests were also monitored via a high speed thermal image camera which showed an increase in temperature between 5 degrees C and 15 degrees C depending on the stretch conditions. POLYM. ENG. SCI., 2012. (c) 2011 Society of Plastics Engineers