Cu(In, Ga)Se-2 (CIGS) thin films are co-evaporated at a constant substrate temperature of 500 degrees C on the Mo/soda lime glass substrates. The structural properties and chemical composition of the CIGS films are studied by an X-ray diffractometer (XRD) and an X-ray fluorescent spectrometer (XRF), respectively. A scanning electron microscope (SEM) is used to study the surface morphology. Lots of uncommon triangle islands and cavities are found on some planes of the CIGS thin films. We investigate the formation mechanism of these triangle islands. It is found that the planes with the triangle islands are (1 1 2) planes terminated by Se atoms. Se ad-dimer as a nucleus, Cu diffusion from CIGS grains brings the epitaxial triangle islands which grow with a two-dimensional layered mode. The film with Cu/(Ga + In) = 0.94-0.98 is one key of the formation of these islands. The triangle cavities are formed due to the insufficient coalescence of triangle islands. The growth of triangle islands brings a compact surface with large layered grains and many jagged edges, but no triangle cavity. Finally, we compare the performance of solar cell with triangle islands and layered gains. It is found that the performance of solar cell with large layered gains is improved. (C) 2012 Elsevier B.V. All rights reserved.