Six mixed matrix membranes (MMMs) were prepared using zeolites of 4A and ZSM-5 incorporated in polyimide of Matrimid 5218. Effects of filler type on membrane morphology and pervaporation performance of MMMs were investigated using isopropanol dehydration. In addition, effects of operating temperature (30, 40, 50, and 60 degrees C), feed water concentration (10, 20, 30, and 40 wt.%) and permeate side pressure (0 and 15 torr) on pervaporation performance were studied. Scanning electron microscopy (SEM) analysis showed there were good adhesion between the fillers and the polymer matrix. Zeolite 4A has a better contact with the polymer phase and thereby nearly no void is formed in the MMM structure. Pervaporation were performed based on L16 array of Taguchi method for design of experiments. The results showed that the best separation condition is achieved at temperature, feed water concentration, and permeate pressure of 30 degrees C, 10 wt.% water and 0 torr, respectively. Selectivities of zeolites 4A and ZSM-5 filled MMMs were calculated as 8991 and 3904 compared with 1276 measured for the neat Matrimid 5218 membrane. Permeation rates of the zeolite 4A and ZSM-5 filled MMMs and the neat polymeric membrane were found to be 0.018, 0.016, and 0.013 kg/m(2) h, respectively. (C) 2011 The Institution of Chemical Engineers. Published by Elsevier B.V. All rights reserved.