Tagasaste wood (Chamaecytisus proliferus L.F. ssp palmensis) was characterized, chemical and energy terms, and assessed its potential as a lignocellulosic raw material, and its integral fractionation by auto-hydrolysis and delignification with ethanol. The hydrothermal treatment of the raw material at 175-185 degrees C provided a liquor containing a substantially increased amount of oligomers (between 16.6% and 47.4% as percentages with respect to the content of the raw material in each polymer fraction). A cellulose pulp with autohydrolysis treatment increased yields (53-60%), reduced Kappa number (28.8-34.6) but also viscosity (755-857 mL/g), and decreased paper strength (2.97-5.22 kN m/kg). However, beating ethanol cellulose from tagasaste was found to improve its strength-related properties more markedly than in soda pulp from the same material (tensile index of 44 kN m/kg). (C) 2010 Elsevier Ltd. All rights reserved.