| 제목 |
Adhesion between Rubber Compounds Containing Various Adhesion Promoters and Brass Plated Steel CordsI. Effect of Sulfur Loading in Rubber Compounds |
| 초록 |
The adhesion property between rubber compounds containing different type of adhesion promoters (resinous adhesion promoters, cobalt salt and zinc borate) and the loading amount of sulfur and brass plated steel cord was investigated to understand the effect of sulfur loading in rubber compounds on their adhesion characteristics to the brass plated steel cords. The pull-out force of adhesion sample increased significantly with increasing loading amount of sulfur into the rubber compounds containing resinous adhesion promoters whereas it decreased slightly with increasing loading amount of sulfur into the rubber compounds containing cobalt salt or zinc borate. Under the humidity aging, the best adhesion retention was observed in the rubber compound containing zinc borate and low loading of sulfur. Regardless of type of adhesion promoters, adhesion retention after thermal aging treatments improved with increasing loading amount of sulfur in rubber compounds. The interphases between the rubber compounds and the brass plated steel cords using AES were interpreted in conjunction with adhesion property. |
| 저자 |
전경수 |
| 소속 |
남도대 |
| 키워드 |
brass plated steel cord; rubber compound; adhesion promoter; cobalt salt; zinc borate; resorcinol formaldehyde resin; methylene donor; sulfur; rubber-to-brass adhesion; adhesion interphase; AES; depth profile; adhesion retention; dezincification
|
| E-Mail |
|
| 원문파일 |
초록 보기 |