| 제목 | Thermally cross-linked Poly(MMA-PEGMA-VBC) terpolymer membranes: Synthesis, characterization and CO2/N2 and CO2/CO separation |
| 초록 | The PEG-based polymer membrane has excellent CO2 solubility and shows high potential for CO2 separation. In this article, P (MMA-PEGMA-BC) (MPC) terpolymers with azide groups were synthesized by free radical polymerization using methylmethacrylate (MMA), poly(ethyleneglycol) methylmethacrylate (PEGMA), and vinylbenzyl chloride (VBC). The crosslinked MPA (C_MPA) membrane was prepared by heat treatment of MPA at 185 °C for 6 hours. The synthesis of terpolymers and membranes and their thermal properties were confirmed by 1H-NMR, FT-IR, DSC and TDA analysis. XRD analysis revealed that an amorphous C_MPA membrane without a crystalline pattern was fabricated. The polymer membranes were evaluated through the gas permeability properties (CO2, CO, and N2) at 35°C. |
| 저자 | 최규직1, 김정훈1, 김성민2, 장봉준1, 홍성권3 |
| 소속 | 1한국화학(연), 2노루코일코팅, 3충남대 |
| 키워드 | Membrane gas separation |